1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500mm), HRC45-48; Moffa medja (F300 ~ 500mm), HRC 47-50; Die ta' estrużjoni żgħira (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Għandha tingħata attenzjoni speċjali lill-punti li ġejjin fil-proċess tat-trattament tas-sħana tad-die tal-estrużjoni:
a. Ir-rata tat-tisħin tas-sezzjoni tat-temperatura għolja għandha tkun mgħaġġla, u l-ħin taż-żamma m'għandux ikun twil wisq, sabiex jipprevjeni ħruq żejjed jew sħana żejda tal-moffa tal-estrużjoni. -- ħbub oħxon imsaħħna żżejjed, ħruq żejjed -- elementi ta 'punt ta' tidwib baxx u inklużjoni jinħall;
b. Ittempra l-estrużjoni tal-aluminju die fil-ħin wara t-tifi biex tevita xquq;
c. Meta l-ebusija tad-die tal-estrużjoni tinstab li tkun insuffiċjenti jew irregolari wara t-trattament bis-sħana, għandha tiġi ttemprata, u t-trattament bis-sħana għandu jerġa' jitwettaq skont il-proċess (meta l-valur tal-ebusija jkun inqas minn HRC35, l-ittemprar ma jkunx permess, u t-trattament bis-sħana jitwettaq direttament);
d. Għal die kbir ta 'estrużjoni tal-aluminju jew die lest b'kavità kumplessa, għandu jiżdied proċess ta' tnaqqis tal-istress u ttemprar (biex jiġi eliminat l-istress tal-magni tal-elettriku u tal-magni, jiġifieri, biex jiġi eliminat l-istress termali u l-istress organizzattiv);
e. Għandu jmut it-temperatura taż-żejt tat-tifi tkun? 100 grad biex jiġi żgurat l-effett tat-tifi.