1. The quality of heat treatment of aluminum extrusion die directly affects the service life of the extrusion die. Quenching is to improve the hardness of the mold, and repeated tempering is to improve the toughness of the mold and stabilize the internal structure. The hardness value of mold heat treatment is specified: large aluminum extrusion die (F>500mm), HRC45-48; Moffa medja (F300 ~ 500mm), HRC47-50; Estrużjoni żgħira tmut (F<300mm), HRC48-51; Three points are tested on the same plane of a set of molds, and the hardness value of each point should be qualified within the specified range.
2. Għandha tingħata attenzjoni speċjali lil diversi punti fil-proċess tat-trattament tas-sħana ta 'estrużjoni li tmut:
a. Il-veloċità tat-tisħin tat-taqsima għolja - għandha tkun mgħaġġla, u l-ħin ta 'żamma m'għandux ikun twil wisq, sabiex jiġi evitat li l-estrużjoni tmut minn sħana żejda jew tisħin żejjed, tisħon żejjed - ħbub oħxon, tisħon żejjed {- elementi ta' tidwib baxx u inklużjonijiet jikkawżaw id-dissoluzzjoni;
b. Wara t-tkessiħ, l-estrużjoni tal-aluminju għandha tkun ittemprata fil-ħin biex tevita xquq;
Ċ. Meta l-ebusija ta 'l-estrużjoni ta' l-estrużjoni tinstab li mhix biżżejjed jew irregolari wara t-trattament tas-sħana, l-ittemprar għandu jitwettaq, u t-trattament tas-sħana għandu jerġa 'jkun - imwettaq skond il-proċess (meta l-valur ta' l-ebusija huwa
d. Għal forom kbar ta 'estrużjoni tal-aluminju jew forom lesti b'kavitajiet kumplessi, għandu jiġi miżjud stress - proċess ta' ttemprar (biex telimina l-ipproċessar elettriku u l-istress tal-magni, jiġifieri, biex telimina l-istress termali u l-istress tal-mikrostruttura);
e. It-temperatura taż-żejt tat-tkessiħ tal-moffa għandha tkun ta '100 grad biex tiżgura l-effett ta' tkessiħ.